Void formation during annealing of neutron-irradiated molybdenum
- 1 August 1975
- journal article
- research article
- Published by Taylor & Francis in Philosophical Magazine
- Vol. 32 (2) , 427-430
- https://doi.org/10.1080/14786437508219965
Abstract
Examination by transmission electron microscopy of molybdenum specimens neutron-irradiated at 60°C with doses of 2·16 × 1018 and 10·6 × 1018 fast neutrons cm−2 has revealed the presence of voids with diameters up to 60 Å. This observation corroborates earlier conclusions based on positron annihilation measurements.Keywords
This publication has 4 references indexed in Scilit:
- Changes in positron annihilation characteristics in molybdenum induced by neutron irradiationPhilosophical Magazine, 1975
- A positron annihilation study of the annealing of, and void formation in, neutron-irradiated molybdenumPhilosophical Magazine, 1974
- The efficiency of void formation during annealing of irradiated molybdenumPhilosophical Magazine, 1973
- Void formation during annealing of irradiated molybdenumPhilosophical Magazine, 1972