Wetting and adhesion of water-borne printing inks on surface-modified polyolefins

Publisher Website
Google Scholar
Abstract
Polyolefin films were surface-modified by different methods to improve the wetting and adhesion of water-borne printing inks. Polyethylene (PE) films were treated with corona at various energy levels. Surface-modified PE films were characterized by contact angle measurements and electron spectroscopy for chemical analysis (ESCA). Good wetting was already achieved with treatment at a lower energy level. Various degrees of adhesion were obtained at various degrees of treatment. A hydrophilic monomer, 2-hydroxyethylmethacrylate (HEMA), was polymerized onto the surfaces of polypropylene (PP) with radiation-induced grafting, which was carried out at two different radiation doses. In both cases, a thick, visible layer of polyHEMA was formed on the surface of PP, and satisfactory wetting was already achieved at lower radiation doses. Scanning electron microscopy (SEM) showed that different degrees of roughness were achieved at various radiation doses. Like the case of corona-treated PE, different degrees of adhesion were obtained at different degrees of surface treatment. This study shows that improved wetting alone is not satisfactory for good practical adhesion', regardless of the surface modification method used.