Equilibrium and kinetic studies of the hydrogen-assisted cracking of steel

This publication has 15 references indexed in Scilit:

• A technique for determining the elemental composition of fracture surfaces produced by crack growth in hydrogen and in water vapor
  Scripta Metallurgica, 1976
• Equilibrium aspects of hydrogen-induced cracking of steels
  Acta Metallurgica, 1974
• Correlation between stretched zone size and fracture toughness
  Engineering Fracture Mechanics, 1974
• Ductile versus brittle behaviour of crystals
  Philosophical Magazine, 1974
• The configuration of moving crack tip zones
  Engineering Fracture Mechanics, 1973
• Chemisorption of hydrogen on iron
  Journal of Catalysis, 1972
• Non-Destructive characterization of hydrogen-embrittlement cracking by acoustic emission techniques
  Engineering Fracture Mechanics, 1971
• Elastic field equations for blunt cracks with reference to stress corrosion cracking
  International Journal of Fracture, 1967
• XXX. The lowering of fracture-stress due to surface adsorption
  Philosophical Magazine, 1956
• Delayed Fracture of Metals under Static Load
  Nature, 1952