Factors Controlling the Sintering of Ceramic Particulate Composites: II, Coated Inclusion Particles
- 1 August 1992
- journal article
- Published by Wiley in Journal of the American Ceramic Society
- Vol. 75 (8) , 2066-2070
- https://doi.org/10.1111/j.1151-2916.1992.tb04466.x
Abstract
No abstract availableKeywords
This publication has 13 references indexed in Scilit:
- Factors Controlling the Sintering of Ceramic Particulate Composites: I, Conventional ProcessingJournal of the American Ceramic Society, 1992
- Microencapsulation of silicon nitride particles with yttria and yttria-alumina precursorsJournal of Materials Research, 1990
- Preparation and properties of uniformly coated inorganic colloidal particles. 2. Chromium hydrous oxide on hematiteLangmuir, 1988
- Preparation and Properties of Coated, Uniform, Inorganic Colloidal Particles: I, Aluminum (Hydrous) Oxide on Hematite, Chromia, and TitaniaAdvanced Ceramic Materials, 1987
- Sintering with Rigid InclusionsJournal of the American Ceramic Society, 1987
- Viscoelastic stresses and sintering damage in heterogeneous powder compactsActa Metallurgica, 1986
- Preparation and Sintering of Monosized Al2O3‐TiO2 Composite PowderJournal of the American Ceramic Society, 1986
- Interactions of precipitated hematite with preformed colloidal titania dispersionsJournal of Colloid and Interface Science, 1986
- Sintering behavior of bi-modal powder compactsActa Metallurgica, 1984
- The thermal expansion of particulate-reinforced compositesJournal of Materials Science, 1982