Hydrophobic recovery of repeatedly plasma-treated silicone rubber. Part 2. A comparison of the hydrophobic recovery in air, water, or liquid nitrogen
- 1 January 1996
- journal article
- Published by Taylor & Francis in Journal of Adhesion Science and Technology
- Vol. 10 (4) , 351-359
- https://doi.org/10.1163/156856196x00751
Abstract
Surfaces of medical grade silicone rubber (Q7-4750, Dow Corning) were modified by repeated (six times) RF plasma treatments using various discharge gases: oxygen, argon, carbon dioxide, and ammonia. The treated samples were stored for a period of 3 months in ambient air, water, or liquid nitrogen. Subsequently, the temporal behavior of the effects of the plasma treatment on the physicochemical surface properties of the silicone rubber was investigated using water contact angle measurements and X-ray photoelectron spectroscopy (XPS). Hydrophobic recovery during 3 months storage in ambient air was considerable and nearly complete for all four plasmas used. Hydrophobic recovery was almost completely suppressed during storage in liquid nitrogen, and only a minor increase of around 10° in advancing water contact angle was observed for all four plasma treatments. Also during storage of treated samples in water, hydrophobic recovery was minimal and initiated again by returning the treated samples to ambient air. XPS analyses showed that argon, carbon dioxide, and ammonia plasma-treated silicone rubber all had increased carbon percentages at the expense of oxygen and silicon after storage in water, or in liquid nitrogen, compared with after storage in ambient air. Interestingly, the carbon content of oxygen plasma-treated silicone rubber decreased during storage in water, or in liquid nitrogen, compared with storage in ambient air, while its oxygen and silicon percentages increased.Keywords
This publication has 14 references indexed in Scilit:
- Hydrophobic recovery of repeatedly plasma-treated silicone rubber. Part 1. Storage in airJournal of Adhesion Science and Technology, 1995
- Plasma treatment of polydimethylsiloxaneJournal of Adhesion Science and Technology, 1994
- Ice adhesion to rubber materialsJournal of Adhesion Science and Technology, 1994
- Plasma surface modification of polyethylene: short-term vs. long-term plasma treatmentJournal of Adhesion Science and Technology, 1993
- Aging effects of repeatedly glow-discharged polyethylene: influence on contact angle, infrared absorption, elemental surface composition, and surface topographyJournal of Adhesion Science and Technology, 1991
- On the aging of oxygen plasma-treated polydimethylsiloxane surfacesJournal of Colloid and Interface Science, 1990
- Dynamics of macromolecules: A challenge for surface analysisSurface and Interface Analysis, 1989
- Contact angle hysteresis on oxygen plasma treated polypropylene surfacesJournal of Colloid and Interface Science, 1989
- Low-molecular-weight materials on corona-treated polypropyleneJournal of Adhesion Science and Technology, 1989
- Surface modification and evaluation of some commonly used catheter materials. I. Surface propertiesJournal of Biomedical Materials Research, 1983