The Influence of Strain Rate on Dislocation Structures in γ/α2 Titanium Aluminides Deformed at 815°C
- 1 January 1990
- journal article
- Published by Springer Nature in MRS Proceedings
Abstract
No abstract availableKeywords
This publication has 7 references indexed in Scilit:
- Mechanical properties and dislocation structures of TiAl single crystals deformed at 4.2–293 KActa Metallurgica et Materialia, 1990
- Deformation of polysynthetically twinned crystals of TiAl with a nearly stoichiometric compositionPhilosophical Magazine A, 1990
- Deformation mechanisms in the intermetallic compound TiAlPhilosophical Magazine A, 1990
- Stoichiometry effects: on the deformation of binary TiAl alloysJournal of Materials Research, 1989
- Weak-beam observation of a dissociation transition in TiAlPhilosophical Magazine A, 1988
- Possible factors affecting the brittleness of the intermetallic compound TiAl. II. Peierls manyvalley reliefScripta Metallurgica, 1988
- The plastic deformation of TiAlMetallurgical Transactions, 1974