Thermal stability of (HfO2)x(Al2O3)1−x on Si
- 28 October 2002
- journal article
- Published by AIP Publishing in Applied Physics Letters
- Vol. 81 (19) , 3618-3620
- https://doi.org/10.1063/1.1519733
Abstract
The kinetics of the interfacial layer (IL) growth between Hf aluminates and the Si substrate during high-temperature rapid thermal annealing (RTA) in either N-2 (similar to10 Torr) or high vacuum (similar to2x10(-5) Torr) is studied by high-resolution x-ray photoelectron spectroscopy and cross-sectional transmission electron microscopy. The significant difference of the IL growth observed between high vacuum and relatively oxygen-rich N-2 annealing (both at 1000 degreesC) is shown to be caused by the oxygen species from the annealing ambient. Our results also show that Hf aluminates exhibit much stronger resistance to oxygen diffusion than pure HfO2 during RTA in N-2 ambient, and the resistance becomes stronger with more Al incorporated into HfO2. This observation is explained by the combined effects of (i) smaller oxygen diffusion coefficient of Al2O3 than HfO2, and (ii) higher crystallization temperature of the Hf aluminates. (C) 2002 American Institute of Physics.Keywords
This publication has 7 references indexed in Scilit:
- Energy gap and band alignment for (HfO2)x(Al2O3)1−x on (100) SiApplied Physics Letters, 2002
- Chemical interaction between atomic-layer-deposited HfO2 thin films and the Si substrateApplied Physics Letters, 2002
- Electrical and physical characteristics of ultrathin hafnium silicate films with polycrystalline silicon and TaN gatesApplied Physics Letters, 2002
- Ultrathin (<4 nm) SiO2 and Si–O–N gate dielectric layers for silicon microelectronics: Understanding the processing, structure, and physical and electrical limitsJournal of Applied Physics, 2001
- High-κ gate dielectrics: Current status and materials properties considerationsJournal of Applied Physics, 2001
- Thermal stability of ultrathin ZrO2 films prepared by chemical vapor deposition on Si(100)Applied Physics Letters, 2001
- Hafnium and zirconium silicates for advanced gate dielectricsJournal of Applied Physics, 2000