Simulation of the fast neutron void swelling in AISI 316 stainless steel. Dose and dose-rate dependences
- 31 January 1977
- journal article
- Published by Elsevier in Journal of Nuclear Materials
- Vol. 64 (1-2) , 115-120
- https://doi.org/10.1016/0022-3115(77)90014-9
Abstract
No abstract availableThis publication has 15 references indexed in Scilit:
- Dose-rate dependence of swelling and damage in ion-irradiated nickelJournal of Nuclear Materials, 1975
- The effects of cold working and pre-irradiation heat treatment on void formation in neutron-irradiated type 316 stainless steelJournal of Nuclear Materials, 1975
- Re-irradiation effect on nucleation of voids in stainless steelJournal of Nuclear Materials, 1975
- Effet du flux instantane sur le gonflement du cuivre pur irradie aux neutrons rapidesJournal of Nuclear Materials, 1973
- Etude de la formation des cavités dans le cuivre irradie aux ions cuivre de 500 keVJournal of Nuclear Materials, 1973
- A direct measurement of gross swelling in nickel-ion-bombarded stainless steelJournal of Nuclear Materials, 1973
- Modele pour la croissance des cavites sous irradiationJournal of Nuclear Materials, 1972
- The dose dependence of void swelling in A.I.S.I. 316 stainless steel during 20 MeV C++ irradiation at 525 °CJournal of Nuclear Materials, 1971
- Void formation in nickel during 20 MeV C++ irradiation at 525 °CJournal of Nuclear Materials, 1971
- The use of ion accelerators to simulate fast neutron-induced voidage in metalsJournal of Nuclear Materials, 1970