Superconducting Tl-Ba-Ca-Cu-O films by sputtering
- 21 November 1988
- journal article
- Published by AIP Publishing in Applied Physics Letters
- Vol. 53 (21) , 2102-2104
- https://doi.org/10.1063/1.100501
Abstract
Superconducting Tl-Ba-Ca-Cu-O thin films 0.2–1.0 μm thick have been prepared on MgO(100) and SrTiO3(100) substrates by dc diode sputtering using a single oxide target. Films containing primarily the Tl2Ba2Ca1Cu2O8 phase were obtained with a Tc (R=0) at 102 K and a transport Jc of 104 A/cm2 at 90 K. For the nearly pure phase Tl2Ba2Ca2Cu3O10 films, the Tc’s (R=0) are higher at 116 K and the transport Jc’s at 100 K are of 105 A/cm2. Both types of films show a strong preferred orientation with the c axis perpendicular to the film plane. The rocking curve of the Tl2Ba2Ca2Cu3O10 films is 0.32° wide and the typical grain size is over 10 μm.Keywords
This publication has 8 references indexed in Scilit:
- Highly oriented superconducting Tl-Ca-Ba-Cu oxide thin films with 2-1-2-2 phaseApplied Physics Letters, 1988
- Sequential electron beam evaporated films of Tl2CaBa2Cu2Oy with zero resistance at 97 KApplied Physics Letters, 1988
- Superconducting Tl-Ca-Ba-Cu-O thin films with zero resistance at temperatures of up to 120 KApplied Physics Letters, 1988
- Crystal Structure of Tl 2 Ba 2 Ca 2 Cu 3 O 10 , a 125 K SuperconductorScience, 1988
- 100-K superconducting phases in the Tl-Ca-Ba-Cu-O systemPhysical Review Letters, 1988
- Superconductivity in the rare-earth-free Tl–Ba–Cu–O system above liquid-nitrogen temperatureNature, 1988
- A New High-Tc Oxide Superconductor without a Rare Earth ElementJapanese Journal of Applied Physics, 1988
- Superconducting Y-Ba-Cu-O oxide films by sputteringApplied Physics Letters, 1987