Large enhancement of yield stress of metals by surface etching in ultra-high vacuum
- 1 September 1997
- journal article
- Published by Elsevier in Scripta Materialia
- Vol. 37 (5) , 699-705
- https://doi.org/10.1016/s1359-6462(97)00152-8
Abstract
No abstract availableFunding Information
- Ministry of Education, Culture, Sports, Science and Technology
This publication has 11 references indexed in Scilit:
- An environmental effect as the major cause for room-temperature embrittlement in FeAlPublished by Elsevier ,2003
- Kinetic and equilibrium effects in the environmental embrittlement of ordered intermetallicsScripta Metallurgica et Materialia, 1995
- The influence of chromium addition on the environmental embrittlement of Ni3(Si,Ti) alloys at ambient temperaturesScripta Metallurgica et Materialia, 1995
- Room-temperature environmental embrittlement in a TiAl alloyScripta Metallurgica et Materialia, 1992
- Environmental effects on room-temperature ductility and fracture in Fe3AlScripta Metallurgica et Materialia, 1990
- Intergranular hydrogen embrittlement of Co3TiScripta Metallurgica, 1985
- Surface oxide softening of polycrystalline molybdenum and tungstenScripta Metallurgica, 1980
- Surface oxide softening in tungsten and molybdenum single crystalsScripta Metallurgica, 1978
- Surface oxide softening of niobium single crystalsActa Metallurgica, 1977
- Surface oxide softening of Nb and Ta single crystalsScripta Metallurgica, 1975