(011)γ/(101)γorder twin of γ lamella in a Ti-40 at.% Al alloy
- 1 January 1992
- journal article
- research article
- Published by Taylor & Francis in Philosophical Magazine A
- Vol. 65 (1) , 15-28
- https://doi.org/10.1080/01418619208201476
Abstract
Transmission electron microscopic study on a α2 + γ two-phases Ti-40 at.% Al alloy demonstrates that (011)γ/(101)γ twin does occur in TiAl. Differently-orientated γ regions are observed to coexist within the same γ lamella with the (011)γ/(101)γ twin plane as their boundary. The variants pair corresponding to these differently-orientated γ regions should come from variants which have the same stacking sequence. The mechanism for the formation of (011)γ/(101)γ twin plane is suggested to grow from the ‘APB-induced fault’ formed in the γ lamella during the precipitation transformation of α2→α2 + γ. Total strain induced by the structure change (h.c.p.→f.c.c.) and by the tetragonality of γ phase during the precipitation transformation can be minimized by a composite of {111}γ and {011}γ twins coexisting in γ lamellae.Keywords
This publication has 12 references indexed in Scilit:
- Orientation relationships between γ plates and α2 matrix in a Ti-39 at.%Al alloyScripta Metallurgica et Materialia, 1990
- Antiphase domains and {011} twins in TiAlPhilosophical Magazine Letters, 1990
- Effect of purity and second phase on ductility of TiAlScripta Metallurgica, 1988
- Twin relationships in TiAlScripta Metallurgica, 1988
- Overview no. 67 The deformation twinning of superlattice structures derived from disordered B.C.C. or F.C.C. solid solutionsActa Metallurgica, 1988
- Pseudotwinning and pseudoelasticity in β Fe-Be alloysActa Metallurgica, 1979
- Fatigue deformation of TiAl base alloysMetallurgical Transactions A, 1977
- The deformation and fracture of TiAl at elevated temperaturesMetallurgical Transactions A, 1975
- On order twinning in AuCuActa Metallurgica, 1964
- Study of CuAu I by transmission electron microscopyActa Metallurgica, 1962