Defect structures at the GaAs/Si interface after annealing
- 13 July 1987
- journal article
- conference paper
- Published by AIP Publishing in Applied Physics Letters
- Vol. 51 (2) , 130-132
- https://doi.org/10.1063/1.98591
Abstract
High-resolution electron microscopy was applied to investigate the effect of post-annealing on the defect structure at the GaAs/Si interface. This study indicates that annealing results in dislocation rearrangement at the interface to form the majority of Lomer’s dislocations with their Burgers vectors parallel to the interface. Dislocations with inclined Burgers vectors (type 2) at the interface after annealing are often observed at steps introduced by the substrate surface roughness. This observation is discussed in terms of the shrinking of stacking faults and microtwins and the preferential nucleation of both stacking faults (or microtwins) and type 2 dislocations at surface steps.Keywords
This publication has 4 references indexed in Scilit:
- Defect reduction by thermal annealing of GaAs layers grown by molecular beam epitaxy on Si substratesApplied Physics Letters, 1987
- Material properties of high-quality GaAs epitaxial layers grown on Si substratesJournal of Applied Physics, 1986
- High resolution electron microscopy of misfit dislocations in the GaAs/Si epitaxial interfaceApplied Physics Letters, 1986
- Metal-semiconductor field-effect transistors fabricated in GaAs layers grown directly on Si substrates by molecular beam epitaxyApplied Physics Letters, 1984