New, fast corroding high ductility Mg–Bi–Ca and Mg–Bi–Si alloys, with no clinically observable gas formation in bone implants
- 1 December 2011
- journal article
- Published by Elsevier in Materials Science and Engineering: B
- Vol. 176 (20) , 1653-1659
- https://doi.org/10.1016/j.mseb.2011.07.011
Abstract
No abstract availableKeywords
This publication has 16 references indexed in Scilit:
- In vivo corrosion and corrosion protection of magnesium alloy LAE442☆Acta Biomaterialia, 2010
- Magnesium hydroxide temporarily enhancing osteoblast activity and decreasing the osteoclast number in peri-implant bone remodelling☆Acta Biomaterialia, 2010
- The history of biodegradable magnesium implants: A review☆Acta Biomaterialia, 2010
- MgZnCa glasses without clinically observable hydrogen evolution for biodegradable implantsNature Materials, 2009
- Degradable biomaterials based on magnesium corrosionPublished by Elsevier ,2009
- Biodegradable magnesium scaffolds: Part II: Peri‐implant bone remodelingJournal of Biomedical Materials Research Part A, 2007
- Biodegradable magnesium scaffolds: Part 1: Appropriate inflammatory responseJournal of Biomedical Materials Research Part A, 2007
- Biodegradable magnesium–hydroxyapatite metal matrix compositesBiomaterials, 2007
- In vitro and in vivo corrosion measurements of magnesium alloysPublished by Elsevier ,2005
- In vivo corrosion of four magnesium alloys and the associated bone responseBiomaterials, 2005