The effect of tempering temperature on near- threshold fatigue crack behavior in quenched and tempered 4140 steel
- 1 October 1988
- journal article
- Published by Springer Nature in Metallurgical Transactions A
- Vol. 19 (10) , 2497-2502
- https://doi.org/10.1007/bf02645477
Abstract
No abstract availableKeywords
This publication has 18 references indexed in Scilit:
- FATIGUE CRACK TIP MECHANICS OF A POWDER METALLURGY ALUMINUM ALLOY IN VACUUM AND HUMID AIRFatigue & Fracture of Engineering Materials & Structures, 1984
- Fatigue crack micromechanisms in ingot and powder metallurgy 7xxx aluminum alloys in air and vacuumActa Metallurgica, 1983
- The micro-mechanisms of tempered martensite embrittlement in 4340-type steelsMetallurgical Transactions A, 1983
- THE EFFECT OF WATER VAPOR ON FATIGUE CRACK TIP MECHANICS IN 7075‐T651 ALUMINUM ALLOYFatigue & Fracture of Engineering Materials & Structures, 1983
- ON THE TRANSITION FROM NEAR‐THRESHOLD TO INTERMEDIATE GROWTH RATES IN FATIGUEFatigue & Fracture of Engineering Materials & Structures, 1983
- A geometric model for fatigue crack closure induced by fracture surface roughnessMetallurgical Transactions A, 1982
- Some considerations on fatigue crack closure at near-threshold stress intensities due to fracture surface morphologyMetallurgical Transactions A, 1982
- Oxide-Induced Crack Closure: An Explanation for Near-Threshold Corrosion Fatigue Crack Growth BehaviorMetallurgical Transactions A, 1981
- Microstructural effects on fatigue crack growth in a low carbon steelMetallurgical Transactions A, 1979
- Influence of microstructure on near-threshold fatigue-crack propagation in ultra-high strength steelMetal Science, 1977