The fracture of constituent particles during fatigue
- 1 October 1982
- journal article
- Published by Elsevier in Materials Science and Engineering
- Vol. 56 (1) , 63-71
- https://doi.org/10.1016/0025-5416(82)90182-3
Abstract
No abstract availableThis publication has 14 references indexed in Scilit:
- A theory of fatigue crack initiation at inclusionsMetallurgical Transactions A, 1982
- Dislocation distribution and prediction of fatigue damageMetallurgical Transactions A, 1981
- Statistical aspects of fatigue crack nucleation from particlesMetallurgical Transactions A, 1980
- Fatigue Crack initiation and microcrack growth in 2024-T4 and 2124-T4 aluminum alloysMetallurgical Transactions A, 1979
- Fatigue crack nucleation at intermetallic particles in alloys — A dislocation pile-up modelScripta Metallurgica, 1979
- The effect of intermetallics composition and microstructure on fatigue crack initiation in AI 2219-T851Metallurgical Transactions A, 1978
- (E) Effect of oxide inclusions on fatigue failureInternational Metals Reviews, 1977
- Fatigue crack initiation and early propagation in Al 2219-T851Metallurgical Transactions A, 1976
- Initiation of fatigue cracks in commercial aluminium alloys and the subsequent propagation of very short cracksEngineering Fracture Mechanics, 1975
- The role of inclusions in fatigue crack initiation in an aluminum alloyInternational Journal of Fracture, 1973