On the Nature of Point Defects Assisting Zn Clustering in Al-Zn 10% Alloy
- 1 August 1968
- journal article
- research article
- Published by Taylor & Francis in Philosophical Magazine
- Vol. 18 (152) , 301-307
- https://doi.org/10.1080/00318086.1968.11716233
Abstract
Results of new resistometric investigations on the ageing after cold-work of an Al-Zn 10% alloy, as well as results of previous experiments on this alloy, are analysed in the light of the main different models advanced for the recovery stage III in Al. A new interesting phenomenon observed in the isothermal ageing after low deformation, namely a slowing down of the initial clustering rate by raising the temperature in the neighbourhood of −50°c, appears explicable only by the vacancy model for stage III.Keywords
This publication has 18 references indexed in Scilit:
- Recovery of Electron-Irradiated Aluminum and Aluminum Alloys. III. Stage IIIPhysical Review B, 1967
- Effects of Various Doping Treatments upon the Damage Production and Recovery of Deuteron-Irradiated AluminumPhysical Review B, 1967
- Orsay On the Stage III Recovery of Electron Irradiated AluminiumPhysica Status Solidi (b), 1967
- Reaction kinetics of stage III recovery in aluminium after neutron irradiationPhysica Status Solidi (b), 1966
- On the recovery of aluminium after neutron irradiation at 78°KPhilosophical Magazine, 1965
- Recovery of Pure and Alloyed Aluminum in Stages I and II after 2-MeV Electron IrradiationPhysical Review B, 1965
- Resistivity Increase in Polycrystalline Al Heavily Cold‐ Worked at 78 °KPhysica Status Solidi (b), 1965
- LOW-TEMPERATURE NEUTRON IRRADIATION DAMAGE IN ALUMINUM AND GOLDCanadian Journal of Physics, 1964
- The Influence of the Initial Defect Concentration on the Annealing of Low‐Temperature Irradiated MetalsPhysica Status Solidi (b), 1964
- Recovery Study in Pure and Alloyed Aluminum Following Electron IrradiationPhysical Review B, 1963