Quantitative Analysis of theMisorientation Distribution After theRecrystallisation of Tensile DeformedCopper Single Crystals
Open Access
- 1 January 1991
- journal article
- research article
- Published by Wiley in Texture, Stress, and Microstructure
- Vol. 13 (4) , 213-226
- https://doi.org/10.1155/tsm.13.213
Abstract
Recrystallisation experiments in tensile deformed 100〉- and 111〉-oriented single crystals of high purity copper yielded very accurate information about the orientations of recrystallised grains and deformation microstructure. For a statistical evaluation of the orientation relationships between the dominant recrystallised grains and the deformation microstructure the misorientation distribution function was calculated. The most frequently occurring orientation relationships can be described by coincidence relationships. Always several coincidence relationships are needed to characterise the results. The specimen treatment strongly influences the occurrence of the individual coincidence orientation relationships. A particularly preferred growth of grains with a 30° or 40° 111〉 orientation relationship was not observed.Keywords
This publication has 0 references indexed in Scilit: