High-Luminance Green-Emitting Thin-Film Electroluminescent Devices Using ZnGa2O4:Mn Phosphor
- 1 June 1995
- journal article
- Published by IOP Publishing in Japanese Journal of Applied Physics
- Vol. 34 (6A) , L684-687
- https://doi.org/10.1143/jjap.34.l684
Abstract
A high-luminance green-emitting electroluminescent (EL) device fabricated using a manganese-activated zinc gallate ( ZnGa2O4:Mn) thin-film phosphor in conjunction with a thick barium titanate ceramic insulator has been demonstrated. The green emission was observed in EL devices fabricated using as-deposited ZnGa2O4:Mn thin films prepared by rf magnetron sputtering. A higher luminance was attained for EL devices fabricated using ZnGa2O4:Mn thin films postannealed at 1020° C in an argon atmosphere. A luminance of 710 cd/m2 and a maximum luminous efficiency of 1 lm/W were obtained for a ZnGa2O4:Mn thin-film EL device driven by a sinusoidal voltage at 1 kHz. The device when driven at 60 Hz exhibited a luminance of 230 cd/m2.Keywords
This publication has 6 references indexed in Scilit:
- Cathodoluminescent characteristics of ZnGa2O4 phosphor grown by radio frequency magnetron sputteringJournal of Applied Physics, 1994
- Low Voltage Cathodoluminescence of Mn2+‐Activated ZnGa2 O 4Journal of the Electrochemical Society, 1994
- Photoluminescence of Mn2+‐Activated ZnGa2 O 4Journal of the Electrochemical Society, 1994
- New ultraviolet-transport electroconductive oxide, ZnGa2O4 spinelApplied Physics Letters, 1994
- The ZnGa2 O 4 Phosphor for Low‐Voltage Blue CathodoluminescenceJournal of the Electrochemical Society, 1991
- High-Luminance Green Zn2SiO4:Mn Thin-Film Electroluminescent Devices Using an Insulating BaTiO3 Ceramic SheetJapanese Journal of Applied Physics, 1991