An in vitro investigation of the anodic polarization and capacitance behavior of 316‐L stainless steel

Publisher Website
Google Scholar
Abstract
Determinations were made of how the corrosion‐resistant properties of the passive film on 316‐L stainless steel are influenced by the material's mechanical and surface states, and the variable pH and PO2 conditions of the interstitial fluid.Cold‐rolled and annealed specimens were surface‐prepared, commercially and in the laboratory, respectively, as if for orthopedic implantation. Passive film behavior was studied by the anodic polarization and pulse‐ potentiostatic capacitance methods. The pH and PO2 of the Ringer's test solution were varied to include interstitial fluid values occurring postoperatively and onto recovery.The anodic polarization behavior of all specimens was found to be pH‐ and PO2‐independent. Breakdown potentials of annealed specimens were 800–950 mV (SCE), in contrast to previously reported values of approximately 350 mV. This substantial increase is related to the influence of surface preparation and, in particular, to the optimization of electropolishing time which acts to produce a microscopically smooth surface, free of debris and disarrayed material. Capacitance behavior of annealed material for potentials > 400 mV was consistent with a model involving the entry of chloride and metal ions (mostly Fe) into the passive film. This entry is related to the onset of pitting.

This publication has 17 references indexed in Scilit: