Temperature-responsive bioconjugates. 1. Synthesis of temperature-responsive oligomers with reactive end groups and their coupling to biomolecules

Publisher Website
Google Scholar
Abstract
Using 3-mercaptopropionic acid (MPA) as a chain-transfer agent, the radical oligomerization of N-isopropylacrylamie (IPAAm) was carried out with varying molar ratios of MPA to IPAAm and DMF. The molecular weight of oligo-IPAAm (OIPAAm) could be controlled by the ratio of MPA to IPAAm. The OIPAAm was confirmed to average one carboxyl end group per chain. All OIPAAms samples were highly water-soluble at lower temperatures and exhibited phase separation near 32 degrees C. The optical transmittance of the OIPAAms aqueous solutions changed drastically at 32 degrees C which was independent of OIPAAms molecular weight. In aqueous solutions of OIPAAm having concentrations higher than 1 wt% and molecular weight of 6100, the oligomers were precipitated and recovered in 85 wt% yield of their original content. Further, OIPAAm was grafted to atelo collagen by activated ester-amine coupling. The OIPAAm-collagen conjugates were able to dissolved in cold water and precipitated at 34 degrees C. Temperature-responsive OIPAAm-collagen conjugates are expected to maintain native collagen functionality in the solution state, react at lower temperatures, and be easily removed from the system with small temperature increases.

This publication has 0 references indexed in Scilit: