EFFECTS OF CRACK CLOSURE AND MEAN STRESS ON THE THRESHOLD STRESS INTENSITY FACTOR FOR FATIGUE OF AN ALUMINIUM CASTING ALLOY,
- 1 November 1990
- journal article
- Published by Wiley in Fatigue & Fracture of Engineering Materials & Structures
- Vol. 13 (6) , 615-624
- https://doi.org/10.1111/j.1460-2695.1990.tb00631.x
Abstract
No abstract availableThis publication has 18 references indexed in Scilit:
- CASTING DEFECTS AND THE FATIGUE BEHAVIOUR OF AN ALUMINIUM CASTING ALLOYFatigue & Fracture of Engineering Materials & Structures, 1990
- THE INFLUENCE OF TEST VARIABLES ON THE FATIGUE CRACK GROWTH THRESHOLDFatigue & Fracture of Engineering Materials & Structures, 1989
- The effect of contact stress intensity factors on fatigue crack propagationTheoretical and Applied Fracture Mechanics, 1984
- Relationships Between Low-Cycle Fatigue and Fatigue Crack Growth Rate PropertiesJournal of Testing and Evaluation, 1979
- THE THRESHOLD STRESS INTENSITY RANGE IN FATIGUEFatigue & Fracture of Engineering Materials & Structures, 1979
- The influence of grain size on threshold stress intensity for fatigue crack growth in AISI 316 stainless steelScripta Metallurgica, 1978
- High cycle fatigue crack propagation under random and constant amplitude loadingsInternational Journal of Pressure Vessels and Piping, 1976
- A study of crack closure in fatigueEngineering Fracture Mechanics, 1974
- Influence of strength and stress history on growth and stabilisation of fatigue cracksEngineering Fracture Mechanics, 1972
- Elastic displacements for various edge-cracked plate specimensInternational Journal of Fracture, 1968