Abrasion phenomena in twill tencel fabric

Publisher Website
Google Scholar
Abstract
The abrasion characteristics of Tencel fabrics were evaluated by Martindale abrasion and laundering, and the breakdown mechanism of fibers was surveyed by scanning electron microscopy. The fabric was subjected to pad‐dry‐cure treatment with two different types of modified dimethyloldihydroxyethylene urea resins (Reaktant DH and Reaktant FC). Although the degree of dry abrasion varied with different resins, the damage exhibited by individual fibers differed little from untreated to resin‐treated; the major mechanism of abrasion was through friction, and the mechanism of fiber failure was multiple splitting and transverse cracking. In untreated Tencel, the characteristic feature of wet abrasion was massive fibrillation, and in crosslinked fabrics, the wet abrasion mechanism was through fiber slippage and slicing action, although in the Reaktant FC‐treated fabric, the wet abrasion mechanism was more through slicing than through fiber splitting. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 1391–1398, 2006

This publication has 20 references indexed in Scilit: