Use of ionic bombardment to increase the conductivity of metallized thin plastic films for making source mounts

Publisher Website
Google Scholar
Abstract
A study was made of the conductivity of thin flexible collodion films metallized either with gold (99.95%) or with gold – 18% palladium alloy and the results obtained were compared with the conductivity of VYNS (a polyvinylchloride–acetate copolymer) films coated with the same metals. For both types of films the conductivity is better with the alloy, especially for VYNS. VYNS films coated with gold or the alloy show better conductivity than collodion coated with either metal. However, ionic bombardment of the collodion films prior to metal coating considerably improves their conductivity, especially with the Au – 8% Pd alloy. For this' alloy the conductivity goes up by a factor of 100 to 1 000 000, and then becomes better than that obtained with VYNS. Although ionic bombardment had a less pronounced effect on the VYNS, an improvement in conductivity was still observed.On a fait une étude comparative de la conductivité de films minces de collodion et de VYNS métallisés soit avec de l'or, soit avec un alliage or – 18% palladium, en couches variant de 2 à 30 μg/cm2. Pour les deux types de films, la conductivité s'est révélée meilleure avec l'alliage; de plus le VYNS devient plus facilement conducteur que le collodion. Toutefois, les films de collodion soumis à un bombardement ionique avant leur métallisation sont beaucoup plus faciles à rendre conducteurs et leur conductivité devient même supérieure à celle obtenue avec les films de VYNS métallisés par l'alliage. Quoique le bombardement ionique ait un effet moins prononcé sur la conductivité subséquente des films de VYNS, elle est tout de même améliorée de façon appréciable. On décrit également des méthodes simples et rapides pour déterminer l'épaisseur des films de collodion et des couches métalliques déposées sur les films.