DETERMINATION OF STRESS CORROSION CRACK INITIATION STRESS AND CRACK VELOCITIES USING SLOWLY STRAINED TAPERED SPECIMENS
- 1 November 1989
- journal article
- Published by Wiley in Fatigue & Fracture of Engineering Materials & Structures
- Vol. 12 (6) , 481-493
- https://doi.org/10.1111/j.1460-2695.1989.tb00558.x
Abstract
No abstract availableThis publication has 9 references indexed in Scilit:
- Localized corrosion and crack initiationMaterials Science and Engineering: A, 1988
- Current Topics in Corrosion:Factors Influencing Stress Corrosion Crack Growth KineticsCorrosion, 1987
- Application of Slow-Strain-Rate Tests to Defining the Stress for Stress Corrosion Crack Initiation in 70/30 BrassPublished by ASTM International ,1984
- Caustic Stress Corrosion Cracking of Mild SteelMetallurgical Transactions A, 1982
- CORROSION FATIGUE OF MILD STEELS IN A SODIUM NITRATE SOLUTIONFatigue & Fracture of Engineering Materials & Structures, 1982
- Predictive approaches to stress corrosion cracking failureCorrosion Science, 1980
- The effect of strain-rate upon stress corrosion crack velocity in α-brass in ammoniacal solutionsCorrosion Science, 1979
- Report on Activities within the European Federation of Corrosion 1977/78British Corrosion Journal, 1979
- Environment Sensitive Fracture and its PreventionBritish Corrosion Journal, 1979