A frictional-wear mechanism for fatigue-crack growth in grain bridging ceramics
- 30 September 1993
- journal article
- Published by Elsevier in Acta Metallurgica et Materialia
- Vol. 41 (9) , 2765-2781
- https://doi.org/10.1016/0956-7151(93)90145-i
Abstract
No abstract availableKeywords
This publication has 18 references indexed in Scilit:
- Cyclic Fatigue from Frictional Degradation at Bridging Grains in AluminaJournal of the American Ceramic Society, 1991
- Cyclic Fatigue of CeramicsJournal of the Ceramic Society of Japan, 1991
- R-curve behaviour of Al2O3 ceramicsActa Metallurgica et Materialia, 1990
- Cyclic Fatigue‐Crack Propagation in Magnesia‐Partially‐Stabilized Zirconia CeramicsJournal of the American Ceramic Society, 1990
- Cyclic fatigue‐crack propagation, stress‐corrosion, and fracture‐toughness behavior in pyrolytic carbon‐coated graphite for prosthetic heart valve applicationsJournal of Biomedical Materials Research, 1990
- Crack‐Resistance Curves of Surface Cracks in AluminaJournal of the American Ceramic Society, 1988
- Crack‐Interface Grain Bridging as a Fracture Resistance Mechanism in Ceramics: II, Theoretical Fracture Mechanics ModelJournal of the American Ceramic Society, 1987
- Crack‐Interface Grain Bridging as a Fracture Resistance I, Mechanism in Ceramics: I, Experimental Study on AluminaJournal of the American Ceramic Society, 1987
- Fatigue in ceramicsInternational Journal of Fracture, 1980
- A Critical Analysis of Crack Propagation LawsJournal of Basic Engineering, 1963