SCC of commercial steels exposed to high hydrogen fugacity
- 1 September 2008
- journal article
- Published by Elsevier in Engineering Failure Analysis
- Vol. 15 (6) , 617-641
- https://doi.org/10.1016/j.engfailanal.2007.10.004
Abstract
No abstract availableKeywords
This publication has 22 references indexed in Scilit:
- An evaluation of steels subjected to rock bolt SCC conditionsEngineering Failure Analysis, 2007
- Atom probe field ion microscope measurements of carbon segregation at an α:α grain boundary and service failures by intergranular stress corrosion crackingCorrosion Science, 2006
- Material influence on the stress corrosion cracking of rock boltsEngineering Failure Analysis, 2005
- Analysis of service stress corrosion cracking in a natural gas transmission pipeline, active or dormant?Engineering Failure Analysis, 2003
- Environmental influence on the stress corrosion cracking of rock boltsEngineering Failure Analysis, 2003
- SCC initiation for X65 pipeline steel in the “high” pH carbonate/bicarbonate solutionCorrosion Science, 2003
- Microstructure and grain boundary microanalysis of X70 pipeline steelJournal of Materials Science, 2003
- Stress corrosion cracking fracture mechanisms in rock boltsJournal of Materials Science, 2003
- Hydrogen in metalsEngineering Failure Analysis, 2001
- Linearly increasing stress test (LIST) for SCC researchMeasurement Science and Technology, 1993