Quantitative analysis of microstructural effects on fatigue crack growth in widmanstätten Ti-6A1-4V and Ti-8Al-1Mo-1V
- 1 January 1979
- journal article
- Published by Elsevier in Engineering Fracture Mechanics
- Vol. 11 (4) , 805-816
- https://doi.org/10.1016/0013-7944(79)90138-3
Abstract
No abstract availableThis publication has 18 references indexed in Scilit:
- Microstructural influences on fatigue and fracture resistance in high strength structural materialsEngineering Fracture Mechanics, 1978
- Enhancement of Fatigue Crack Growth and Fracture Resistance in Ti-6Al-4V and Ti-6Al-6V-2Sn Through Microstructural ModificationJournal of Engineering Materials and Technology, 1977
- Texture stability in heat treated Ti6Al4VMaterials Science and Engineering, 1977
- An analysis of reported fatigue crack growth rate data with special reference to Ti-6A1-4VEngineering Fracture Mechanics, 1977
- Cyclic crack growth and fracture resistance of Ti-6Al-6V-2Sn as influenced by recrystallization anneal and interstitial oxygen contentEngineering Fracture Mechanics, 1975
- Variability in Fatigue Crack Growth Rate TestingJournal of Testing and Evaluation, 1975
- Analysis of Grain- and Particle-Size Distributions in Metallic MaterialsInternational Materials Reviews, 1972
- Linear fracture mechanics, fracture transition, and fracture controlEngineering Fracture Mechanics, 1968
- Fatigue Crack Propagation in MetalsNature, 1966
- A Critical Analysis of Crack Propagation LawsJournal of Basic Engineering, 1963