MULTILAYERED COMPOSITES BASED ON ULTRAHIGH CARBON STEEL AND BRASS
- 1 January 1990
- journal article
- research article
- Published by Taylor & Francis in Materials and Manufacturing Processes
- Vol. 5 (3) , 363-376
- https://doi.org/10.1080/10426919008953258
Abstract
Thermal and mechanical processing procedures were developed to prepare unique metal matrix laminated composites (MMLC) based on a combination of ultra high carbon steel (UHCS) and brass. The MMLC material, of 50 volume percent of each component, was processed at about 700°C to large strains by a combination of rolling and press-bonding. Discrete interlayer boundaries were retained until layer thicknesses of less than 10 μm were reached. At this stage brass penetrated the UHCS material and became the continuous component, The UHCS/brass laminated composites can be selectively heat-treated with no interdiffusion between the layers. Exceptional ductility was obtained in the laminated composite in bend and tensile tests at room temperature.Keywords
This publication has 11 references indexed in Scilit:
- Mechanical Properties of Discontinuous SiC Reinforced Aluminum Composites at Elevated TemperaturesJournal of Engineering Materials and Technology, 1988
- Internal Stress Superplasticity in 2024 Al-SiC Whisker Reinforced CompositesJournal of Composite Materials, 1988
- Deformation behaviour of coextruded multilayer composites with polycarbonate and poly(styrene-acrylonitrile)Journal of Materials Science, 1987
- Superplasticity of a stainless steel clad ultrahigh carbon steelMetallurgical Transactions A, 1986
- Fibre-reinforced metal-matrix compositesComposites, 1985
- Superplastic behavior in ferrous laminated compositesActa Metallurgica, 1984
- Creep rupture of a silicon carbide reinforced aluminum compositeMetallurgical Transactions A, 1984
- Superplastic bonding of ferrous laminatesScripta Metallurgica, 1979
- Formability of sandwich sheet materials in plane strain compression and rollingMetallurgical Transactions A, 1979
- Absolute interfacial energies of [001] tilt and twist grain boundaries in copperActa Metallurgica, 1959