Microstructural Features of Flow Instability in α-Titanium Cylinders under High Strain Rate Compression at 25°C to 400 °C
- 1 November 1993
- journal article
- Published by Springer Nature in Metallurgical Transactions A
- Vol. 24 (11) , 2513-2520
- https://doi.org/10.1007/bf02646530
Abstract
No abstract availableKeywords
This publication has 10 references indexed in Scilit:
- Processing map for controlling microstructure in hot working of hot isostatically pressed powder metallurgy NIMONIC AP-1 superalloyMetallurgical Transactions A, 1992
- Influence of oxygen on dynamic recrystallization during hot working of polycrystalline copperMaterials Science and Engineering: A, 1992
- Processing map for hot working of powder Metallurgy 2124 Al-20 Vol Pct SiCp Metal Matrix CompositeMetallurgical Transactions A, 1992
- Characterization of hot deformation behavior of brasses using processing maps: Part II. β Brass and α-β brassMetallurgical Transactions A, 1991
- Characterization of hot deformation behavior of brasses using processing maps: Part I. α BrassMetallurgical Transactions A, 1991
- Dynamic recrystallization during hot deformation of aluminum: A study using processing mapsMetallurgical Transactions A, 1991
- Processing map for hot working of alpha-zirconiumMetallurgical Transactions A, 1991
- Plastic instability and flow localization in shear at high rates of deformationActa Metallurgica, 1984
- The Occurrence of Shear Bands in MetalworkingPublished by Springer Nature ,1983
- Plastic stability in tension and compressionActa Metallurgica, 1976