Formation of B2 antiphase domains in rapidly solidified Fe-Al alloys
- 1 October 1991
- journal article
- research article
- Published by Taylor & Francis in Philosophical Magazine A
- Vol. 64 (4) , 797-805
- https://doi.org/10.1080/01418619108213949
Abstract
Fe-Al-X (X = Cr, Mo) alloys in the composition range 50 to 80 at.% Fe, 0 to 20 at.% X were rapidly solidified by chill-block melt-spinning. Thin foil transmission electron microscopy of the rapidly solidified ribbons revealed that antiphase domains occur in the B2 structure in the limited composition range 22 to 37 at.% Al. The B2 antiphase domain size was found to increase with the increasing Al-content of the ribbon. The criterion for antiphase domain (APD) formation is investigated in terms of mechanisms for formation of the B2 structure.Keywords
This publication has 6 references indexed in Scilit:
- The order-disorder transformation in Ni3Al and Ni3AlFe alloys—II. Phase transformations and microstructuresActa Metallurgica, 1987
- The order-disorder transformation in Ni3Al and Ni3AlFe alloys—I. Determination of the transition temperatures and their relation to ductilityActa Metallurgica, 1987
- Anisotropic antiphase boundaries in rapidly solidified Ni3AlActa Metallurgica, 1985
- Ductile Ordered Intermetallic AlloysScience, 1984
- Improved Strength and Ductility of Ni3Al by Boron Modification and Rapid SolidificationMetallurgical Transactions A, 1984
- The Microstructure of Order-Disorder TransitionsPublished by Springer Nature ,1974