The Fabrication of a Vanadium-Stainless Steel Test Section for MHD Testing of Insulator Coatings in Flowing Lithium

Publisher Website
Google Scholar
Abstract
To test the magnetohydrodynamic (MHD) pressure drop reduction performance of candidate insulator. coatings for the ITER Vanadium/Lithium Breeding Blanket, a test section comprised of a V-4Cr-4Ti liner inside a stainless steel pipe was designed and fabricated. Theoretically, the MHD pressure drop reduction benefit resulting from an electrically insulating coating on a vanadium-lined pipe is identical to the benefit derived from an insulated pipe fabricated of vanadium alone. A duplex test section design consisting of a V alloy liner encased in a SS pressure boundary provided protection for vanadium from atmospheric contamination during operation at high temperature and obviated any potential problems with vanadium welding while also minimizing the amount of V alloy material required. From the MHD and insulator coating point of view, the test section outer SS wall and inner V alloy liner can be modeled simply as a wall having a sandwich construction. Two 52.3 mm OD × 2.9 m long V-alloy tubes were fabricated by Century Tubes from 64 mm × 200 mm × 1245 mm extrusions produced by Teledyne Wah Chang. The test section's duplex structure was subsequently fabricated at Century Tubes by drawing down a SS pipe (2 inch schedule 10) over one of the 53.2 mm diameter V tubes.

This publication has 0 references indexed in Scilit: