The microplastic behaviour of polycrystalline nickel
- 1 September 1964
- journal article
- research article
- Published by Taylor & Francis in Philosophical Magazine
- Vol. 10 (105) , 513-526
- https://doi.org/10.1080/14786436408224227
Abstract
The pre-yield microstrain behaviour of nickel having grain sizes ranging from 0·018 to 0·44 mm has been studied at 298°K. Calculations, based on observations that microstrain proceeds by three stages in the highest purity samples, suggest that the formation of an “incipient glide polygonization cell” in the microstrain region determines the cell size observed after macrodeformation.Keywords
This publication has 8 references indexed in Scilit:
- The substructure of plastically deformed nickelActa Metallurgica, 1964
- Dislocation configurations and the microstrain of polycrystalline berylliumActa Metallurgica, 1963
- Microstraining in αCuAl single crystalsActa Metallurgica, 1963
- On the Yield Stress of Copper CrystalsJournal of Applied Physics, 1962
- Elastic-Plastic Transition in Copper Crystals as Determined by an Etch-Pit TechniqueJournal of Applied Physics, 1961
- Microstrain in polycrystalline metalsActa Metallurgica, 1961
- The early stages of plastic deformation in copperActa Metallurgica, 1959
- Plastic deformation of nickel single crystals at low temperaturesPhilosophical Magazine, 1958