Effects of alloy stoichiometry on environmental embrittlement in Ll2-ordered (Co,Fe)3V alloys
- 1 November 1992
- journal article
- Published by Elsevier in Scripta Metallurgica et Materialia
- Vol. 27 (10) , 1307-1311
- https://doi.org/10.1016/0956-716x(92)90075-p
Abstract
No abstract availableThis publication has 26 references indexed in Scilit:
- An environmental effect as the major cause for room-temperature embrittlement in FeAlPublished by Elsevier ,2003
- Effects of alloy composition on environmental embrittlement of B2 ordered iron aluminidesScripta Metallurgica et Materialia, 1991
- Chromium addition and environmental embrittlement in Fe3AlScripta Metallurgica et Materialia, 1990
- Environmental effects on the mechanical properties of Co3Ti containing boron, carbon and berylliumJournal of Materials Science, 1990
- Environmental embrittlement in boron-free and boron-doped FeAl (40 at. % Al) alloysScripta Metallurgica et Materialia, 1990
- Environmental effects on room-temperature ductility and fracture in Fe3AlScripta Metallurgica et Materialia, 1990
- Mechanical properties of Co3Ti polycrystals alloyed with various additionsJournal of Materials Science, 1989
- The influence of hydrogen on deformation and fracture processes in Co3Ti polycrystals and single crystalsActa Metallurgica, 1989
- Hydrogen embrittlement of pseudobinary l12-type Ni3(Alo.4Mno.6) intermetallic compoundMetallurgical Transactions A, 1988
- Factors affecting the intergranular hydrogen embrittlement of Co3TiActa Metallurgica, 1986