Development of a pelleted waste form for high-level alumina wastes
- 1 September 1980
- report
- Published by Office of Scientific and Technical Information (OSTI)
Abstract
A formulation to pelletize simulated high-level ICPP alumina waste calcine was developed. The pellets are formed on a 41-cm-diameter disc pelletizer using 5% bentonite, 2% metakaolin, and 5 wt % calcium hydroxide as a solid binder and a solution of 7M phosphoric acid and 4M nitric acid as a liquid binder. After drying and heat treatment at 800/sup 0/C for 2 hours, the average crush strength of the pellets is 3.9 MPa and the pellets have a leach resistance of 10/sup -3/ g/cm/sup 2//day, based on Soxhlet leaching for 48 h at 95/sup 0/C with distilled water.Keywords