Fracture of dense, textured Bi2Sr2CaCu2Ox
- 1 April 1993
- journal article
- Published by IOP Publishing in Superconductor Science and Technology
- Vol. 6 (4) , 282-286
- https://doi.org/10.1088/0953-2048/6/4/012
Abstract
Dense, bulk Bi2Sr2CaCu2Ox bars were fabricated by sinter forging. The bars exhibited strong textures in which the c axes of the platelike grains were preferentially aligned parallel to the pressing direction. Fracture strength was measured in four-point bending, and in compression at angles of 0, 45, and 90 degrees to the pressing direction. Maximum strength in tension gas 100 MPa and average strength was 84 MPa. Maximum strength in compression, which depended on orientation, was 180 MPa and maximum average strength was 120-135 MPa.Keywords
This publication has 28 references indexed in Scilit:
- Highly textured Bi-2223 aggregates produced by cold pressing of powdersPhysica C: Superconductivity and its Applications, 1992
- Microstructural and magnetic studies of sinter-forged (Bi, Pb)2Sr2Ca2Cu3Ox superconductorMaterials Letters, 1992
- Mechanical properties and texture of dense polycrystalline Bi2Sr2CaCu2OxSuperconductor Science and Technology, 1992
- Mechanical strength of hot-pressed Bi–Pb–Sr–Ca–Cu–O superconductorJournal of Materials Research, 1992
- Shock consolidation of crystallographically aligned Bi2Sr2CaCu2O8 powdersPhysica C: Superconductivity and its Applications, 1991
- High current density Bi-Sr-Ca-Cu-O superconductor wires produced by hot isostatic pressingSuperconductor Science and Technology, 1991
- Preparation of High-Tc Superconductor in the (BiPbSrCaCuO) System by Hot-Pressing*Japanese Journal of Applied Physics, 1991
- Transmission electron microscope investigation and magnetic properties of HIPed Bi-Pb-Sr-Ca-Cu-OSuperconductor Science and Technology, 1991
- Hot isostatically pressed Bi-Sr-Ca-Cu-OSuperconductor Science and Technology, 1990
- Retrograde Densification in Bi2Sr2CaCu2O8 SuperconductorsJournal of the American Ceramic Society, 1989