The Fatigue Properties of Z-Section Test Pieces Completely Machined from an Aluminium Alloy Extrusion Conforming to D.T.D. 364B

Publisher Website
Google Scholar
Abstract
In 1949 F. H. Pollicutt, in the course of a discussion on a paper presented by P. B. Walker to the Royal Aeronautical Society, reported fatigue test results which indicated that when the aluminium alloy conforming to specification D.T.D.364 was tested, under , axial loads, in the form of Z-sections, its fatigue properties were extremely low. Z-sections with unmachined surfaces and even Z-sections with completely machined surfaces failed after short endurances at stress ranges under which small polished round test pieces would not have failed even after hundreds of millions of cycles. Pollicutt, in discussing these low values, advised that great caution should be exercised in their interpretation, warning equally against an unqualified acceptance of the testing technique and a too facile acceptance of small polished round bar test results.