On the failure mechanism of chemically embrittled Cu3Au single crystals
- 1 April 1986
- journal article
- Published by Springer Nature in Metallurgical Transactions A
- Vol. 17 (4) , 703-710
- https://doi.org/10.1007/bf02643991
Abstract
No abstract availableKeywords
This publication has 17 references indexed in Scilit:
- Brittle behavior of ductile metals during stress-corrosion crackingPhilosophical Magazine A, 1985
- The crystallography of stress corrosion cracking in face centered cubic single crystalsCorrosion Science, 1984
- Concerning the mechanism of transcrystalline stress-corrosion cracking of α-brassScripta Metallurgica, 1984
- Oxide scale induced cleavage fracture in an ODS Fe-Cr-Al alloyMetallurgical Transactions A, 1983
- On the Propagation of Transgranular Stress-Corrosion CracksPublished by Springer Nature ,1983
- Studies of the orientations of fracture surfaces produced in austenitic stainless steels by stress-corrosion cracking and hydrogen embrittlementMetallurgical Transactions A, 1980
- The propagation of transgranular stress-corrosion cracks in admiralty metalMetallurgical Transactions A, 1980
- Stress Corrosion via Localized Anodic Dissolution in Cu-Au AlloysCorrosion, 1969
- On The Electrochemical Behaviors of Copper-Gold AlloysTransactions of the Japan Institute of Metals, 1965
- Electron Metallography of Chemical Attack Upon Some Alloys Susceptible to Stress Corrosion CrackingCorrosion, 1963