The effects of oxide stress waveform on MOSFET performance
- 9 December 2002
- conference paper
- Published by Institute of Electrical and Electronics Engineers (IEEE)
- p. 719-722
- https://doi.org/10.1109/iedm.1991.235322
Abstract
Three different waveforms were used to study the behavior of n-MOSFETs after dynamic oxide stress. It is shown that the transport and detrapping properties of holes generated near the anode can account for the differences observed after unipolar and bipolar oxide stressing. Bipolar stress yields a lower rate of bulk charge trapping and longer time to breakdown than unipolar stress. The difference is dependent on both field and frequency. At the same time, bipolar stress leads to enhanced interface trap generation. Since the gate-drain overlap region of MOSFETs in circuits is subject to bipolar stress, DC transistor stress tests may underestimate the MOSFET degradation rate. The observation that interface trap density does not saturate during bipolar stress as readily as during unipolar stress is particularly alarming. Bidirectional tunneling current creates a larger number of interface traps than does unidirectional gate current. Even though unipolar stressed devices suffer more bulk trapping and TDDB (time-dependent dielectric breakdown) degradation than do bipolar stressed devices, the degradation in transconductance, mobility, and threshold voltage is worse in bipolar stressed devices.<>Keywords
This publication has 4 references indexed in Scilit:
- High-frequency time-dependent breakdown of SiO/sub 2/IEEE Electron Device Letters, 1991
- High-field and current-induced positive charge in thermal SiO2 layersJournal of Applied Physics, 1985
- Electrical breakdown in thin gate and tunneling oxidesIEEE Transactions on Electron Devices, 1985
- Two-carrier nature of interface-state generation in hole trapping and radiation damageApplied Physics Letters, 1981