Fabrication of Bi2Sr2CaCu2Ox High Tc Superconducting Film with H2O Assisted Metalorganic Chemical Vapor Deposition
- 1 November 1992
- journal article
- Published by IOP Publishing in Japanese Journal of Applied Physics
- Vol. 31 (11B) , L1592
- https://doi.org/10.1143/jjap.31.l1592
Abstract
With the objective of the deposition of Bi2Sr2CaCu2O x (BSCCO(2212)) films at low temperature, the metalorganic chemical vapor deposition (MOCVD) has been carried out and c-axis oriented BSCCO(2212) films on MgO(001) substrates were obtained at 550°C and 600°C. When water vapor was added into the reactor, the crystallization of deposited films changed in relation to the partial pressure of water vapor. The more H2O was supplied, the less BSCCO(2212) crystal tended to be formed at 600°C, and the opposite tendency was found at 550°C.Keywords
This publication has 3 references indexed in Scilit:
- Phase Control of Superconducting Bi-Sr-Ca-Cu-O Thin Films Prepared by Laser Ablation MethodJapanese Journal of Applied Physics, 1991
- Effect of Temperature and Oxygen Pressure on Preparation of Bi2Sr2CaCu2Ox Thin Films by Metalorganic DepositionJapanese Journal of Applied Physics, 1991
- Assignment of the Powder X-Ray Diffraction Pattern of Superconductor Bi2(Sr, Ca)3-xCu2OyJapanese Journal of Applied Physics, 1988