High-Tc Superconductor Produced by Oxidization of Melt-Spun Ag-Ho-Ba-Cu Alloy Ribbon
- 1 February 1988
- journal article
- Published by IOP Publishing in Japanese Journal of Applied Physics
- Vol. 27 (2A) , L195
- https://doi.org/10.1143/jjap.27.l195
Abstract
A (Ho0.17Ba0.33Cu0.5)50Ag50 alloy ribbon with a non-equilibrium structure was produced by melt-spinning. Heating of the alloy ribbon in air brought about the structural change to a stable metallic phase at about 610 K, followed by the formation of Ho1Ba2Cu3O6.7 and Ag in the range of 630 to 740 K. The mixed materials of Ho1Ba2Cu3O6.7 and Ag produced by oxidization of the melt-spun ribbon exhibited high-T c superconductivity with onset at 90 K and zero resistance at 80 K. It is notable that the mixture of Ag enables us to produce an alloy ribbon by melt-spinning even in the Ho-Ba-Cu alloy system with large miscibility gap.Keywords
This publication has 12 references indexed in Scilit:
- High-Tc Superconductor Prepared by Oxidization of a Melt-Spun Eu1Ba2Cu3 Alloy RibbonJapanese Journal of Applied Physics, 1987
- Crystal Structure of Ba2HoCu3O7-x Determined by Neutron Powder DiffractionJapanese Journal of Applied Physics, 1987
- Structures and Upper Critical Fields of High Tc Superconductors (RE)Ba2Cu3OxJapanese Journal of Applied Physics, 1987
- High Tc Superconductor Prepared by Oxidization of a Liquid-Quenched Yb1Ba2Cu3 Alloy Foil in AirJapanese Journal of Applied Physics, 1987
- Oxygen and rare-earth doping of the 90-K superconducting perovskitePhysical Review B, 1987
- High Tc Superconductivities of A2Ba4Cu6O14+yJapanese Journal of Applied Physics, 1987
- Structural Properties of a High-Tc Superconductor Ho-Ba-Cu Oxide Studied by Transmission Electron MicroscopyJapanese Journal of Applied Physics, 1987
- Superconductivity above 90 K in Y-Ba-Cu-O Compounds and Their Critical Current Densities at 77 KJapanese Journal of Applied Physics, 1987
- High Tc Magnetic Superconductor: Ho-Ba-Cu OxideJapanese Journal of Applied Physics, 1987
- Preparation of a High Tc Superconductor by Oxidization of an Amorphous La1.8Sr0.2Cu Alloy Ribbon in AirJapanese Journal of Applied Physics, 1987