NO2-sensitive LaFeO3film prepared by thermal decomposition of the heteronuclear complex, {La[Fe(CN)6]·5H2O}x
- 1 January 1993
- journal article
- research article
- Published by Royal Society of Chemistry (RSC) in Journal of Materials Chemistry
- Vol. 3 (7) , 767-769
- https://doi.org/10.1039/jm9930300767
Abstract
Phase pure perovskite-type LaFeO3 powders have been prepared by the thermal decomposition of a cyanidebridged heteronuclear complex. Formation of the perovskite was confirmed for the sample sintered in air at 300 °C for 1 h. The mean particle diameter and the specific surface area were 200 nm and 5 m2 g–1, respectively, (sample density = 6.67 g cm–3) for the LaFeO3 obtained by calcining at 1000 °C. The conductivity of an LaFeO3 thick film formed by sintering at 1000 °C, increased when the measuring atmosphere was changed from air to NO2, and returned to the original level after NO2 was removed above 350 °C. The mechanical strength of the film was improved by sintering with glass resin.Keywords
This publication has 16 references indexed in Scilit:
- NO2 Sensitive Ga-doped ZnO Thin FilmChemistry Letters, 1992
- Preparation of Perovskite-Type Oxide, LaCrO3, by Thermal Decomposition of La[Cr(CH2(COO)2)3]⋅6H2OJournal of the Ceramic Society of Japan, 1992
- Preparation and Properties of Perovskite-Type Oxides from Three-Dimensional Heterometal Assemblies, {Ln[Cr(ox)3]⋅10H2O}x (Ln=La, Pr or Nd)Journal of the Ceramic Society of Japan, 1992
- Preparation of Perovskite-type Oxides with Large Surface Area by Citrate ProcessChemistry Letters, 1987
- OXYGEN-SORPTIVE PROPERTIES OF DEFECT PEROVSKITE-TYPE La1−xSrxCo1−yFeyO3−δChemistry Letters, 1985
- OXYGEN-SORPTIVE PROPERTIES AND DEFECT STRUCTURE OF PEROVSKITE-TYPE OXIDESChemistry Letters, 1984
- Synthesis of LaCrO3 under hydrothermal conditions.Journal of the Ceramic Association, Japan, 1982
- Preparation of Tin Oxide Films from Ultrafine ParticlesJournal of the Electrochemical Society, 1981
- Crystallographic, Electric and Thermochemical Properties of the Perovskite-Type Ln1-xSrxCoO3(Ln: Lanthanoid Element)Japanese Journal of Applied Physics, 1974
- The crystal structure of LaFe(CN)6.5H2OActa Crystallographica Section B: Structural Science, Crystal Engineering and Materials, 1973