Near-threshold corrosion fatigue crack growth behavior of type 422 stainless steel at controlled maximum stress intensities
- 1 April 1984
- journal article
- mechanical behavior
- Published by Springer Nature in Metallurgical Transactions A
- Vol. 15 (4) , 693-699
- https://doi.org/10.1007/bf02644200
Abstract
No abstract availableKeywords
This publication has 21 references indexed in Scilit:
- Influence of oxide-induced crack closure on near-threshold fatigue crack growth behaviorActa Metallurgica, 1982
- Effect of grain size and cold work on the near threshold fatigue crack propagation rate and crack closure in ironScripta Metallurgica, 1982
- Crack growth retardation due to micro-roughness: A mechanism for overload effects in fatigueScripta Metallurgica, 1982
- Low temperature and grain size effects on threshold and fatigue crack propagation in a high strength low alloy steelMaterials Science and Engineering, 1981
- The influence of environment and stress ratio on fatigue crack growth at near threshold stress intensities in low-alloy steelsEngineering Fracture Mechanics, 1980
- Near-threshold fatigue-crack propagation in steelsInternational Materials Reviews, 1979
- Review and extension of compliance information for common crack growth specimensInternational Journal of Fracture, 1978
- Computer-Controlled Decreasing Stress Intensity Technique for Low Rate Fatigue Crack Growth TestingJournal of Testing and Evaluation, 1978
- Threshold Corrosion Fatigue Crack Growth in SteelsJournal of Testing and Evaluation, 1978
- The slow fatigue crack growth and threshold behaviour of a medium carbon alloy steel in air and vacuumEngineering Fracture Mechanics, 1975