The effect of low-frequency cyclic stresses on the initiation of stress corrosion cracks in X60 line pipe steel in carbonate solutions
- 1 January 1983
- journal article
- Published by Elsevier in Corrosion Science
- Vol. 23 (6) , 547-558
- https://doi.org/10.1016/0010-938x(83)90118-x
Abstract
No abstract availableKeywords
This publication has 8 references indexed in Scilit:
- The interaction of strain-rate and repassivation rate in stress corrosion crack propagationCorrosion Science, 1980
- Effects of Cyclic Tensile Loading on Stress Corrosion Cracking Susceptibility for Sensitized Type 304 Stainless Steel in 290 C High Purity WaterCorrosion, 1979
- Die Praktische Bedeutung niedrig‐frequenter Lastwechsel bei dehnungsinduzierter SpannungsrißkorrosionMaterials and Corrosion, 1978
- Strain hardening parameters of some low carbon manganese steelsScripta Metallurgica, 1977
- Creep induced by load cycling in a C-Mn steelActa Metallurgica, 1976
- Stress corrosion crack propagation: A constant charge criterionCorrosion Science, 1975
- Stress Corrosion Cracking of Carbon Steel in Carbonate SolutionsCorrosion, 1972
- The electrochemical parameters of stress-corrosion crackingCorrosion Science, 1968