Temperature dependence of the current in SiO2 in the high field tunneling regime
- 15 June 1984
- journal article
- research article
- Published by AIP Publishing in Journal of Applied Physics
- Vol. 55 (12) , 4322-4329
- https://doi.org/10.1063/1.333044
Abstract
In this work, we study the effect of temperature on the tunneling current in thin SiO2 films (≊200 Å) and show that a reversal of behavior is produced by increasing fields. While in the lower range (≤9 MV/cm) the current is well represented by the Fowler–Nordheim model and increases with temperature, it substantially disagrees with the theory at fields close to breakdown (>10 MV/cm) where it is larger than expected and decreases with increasing temperature. This cannot be explained with the formation of (quasi) stable positive charge which is known to be created by high field stress but, under our experimental conditions, is found to be negligibly small. Therefore, we deal with a new kind of effect for which few different possibilities are suggested as mechanisms at the microscopic level.This publication has 13 references indexed in Scilit:
- Novel Mechanism for Tunneling and Breakdown of Thin SiFilmsPhysical Review Letters, 1983
- Resonant tunneling through quantum wells at frequencies up to 2.5 THzApplied Physics Letters, 1983
- Electron trapping/detrapping within thin SiO2 films in the high field tunneling regimeJournal of Applied Physics, 1983
- On tunneling in metal-oxide-silicon structuresJournal of Applied Physics, 1982
- Fowler-Nordheim electron tunneling in thin Si-SiO2-Al structuresJournal of Applied Physics, 1981
- Electron tunneling at Al-SiO2 interfacesJournal of Applied Physics, 1981
- Current and C-V instabilities in SiO2 at high fieldsApplied Physics Letters, 1977
- Location of positive charges in SiO2 films on Si generated by vuv photons, x rays, and high-field stressingJournal of Applied Physics, 1977
- Tunneling of electrons from Si into thermally grown SiO2Solid-State Electronics, 1977
- Impact ionization and positive charge in thin SiO2 filmsJournal of Applied Physics, 1976