Preparation and Properties of Chromium Films
- 1 May 1968
- journal article
- Published by AIP Publishing in Journal of Applied Physics
- Vol. 39 (6) , 2851-2856
- https://doi.org/10.1063/1.1656683
Abstract
A study was made of the properties of chromium films formed by vacuum deposition techniques. It was found possible to obtain films that had nearly bulk characteristics by using specific deposition conditions. The resistivity was determined as a function of film thickness. The orientation of the films was determined using x-ray diffraction. The film orientation was found to be dependent upon the particular glassy material used as a substrate. The resistance anomaly associated with the antiferromagnetic-paramagnetic transition in bulk chromium was observed. The experimentally determined resistance-temperature relationships for the Cr films were explained in terms of the effects of stress on the magnetic transition temperature.This publication has 18 references indexed in Scilit:
- Field Effect and Electrical Conduction Mechanism in Discontinuous Thin Metal FilmsJournal of Applied Physics, 1966
- The resistivity and structure of chromium thin filmsBritish Journal of Applied Physics, 1965
- Angle-of-Incidence and Stress Effects on Rotating and Stationary SubstratesJournal of Vacuum Science and Technology, 1965
- Relation of Rate and Duration of Evaporation to Background Pressure for the Deposition of Thin Films in VacuumJournal of Applied Physics, 1963
- The effect of fabrication variables on chromium thin film resistorsVacuum, 1963
- Initial study of electrical resistivity of a chromium single crystalJournal of the Less Common Metals, 1962
- Electrical Resistivity of Chromium in the Vicinity of the Néel TemperatureJournal of Applied Physics, 1961
- The transition in chromium and in some alloys of chromium with small amounts of other transition elementsJournal de Physique et le Radium, 1959
- Effect of Plastic Deformation on the Electrical Resistivity of ChromiumNature, 1958
- Compressibilities and Pressure Coefficients of Resistance of Elements, Compounds, and Alloys, Many of Them AnomalousProceedings of the American Academy of Arts and Sciences, 1933