Interfacial reactions of iron thin films on silicon
- 15 June 1985
- journal article
- Published by AIP Publishing in Journal of Applied Physics
- Vol. 57 (12) , 5246-5250
- https://doi.org/10.1063/1.335264
Abstract
Interfacial reactions of iron thin films on silicon have been investigated by transmission electron microscopy. FeSi was found to form after 400 °C annealing. Small amount of Fe3Si was detected in samples annealed at 450 to 500 °C. β-FeSi2 grains were predominant with a few FeSi grains remained in samples annealed at 600 °C. β-FeSi2 was found to be the dominant phase, whereas α-FeSi2 was predominant in samples annealed at 900–1100 °C in N2 ambient and in vacuum, respectively. Two-step annealings were effective in promoting the growth and improving the quality of epitaxial FeSi2. More uniform growth of epitaxial FeSi2 was observed for samples annealed in vacuum than those heat treated in N2 ambient. The mechanisms of epitaxial growth and the influence of impurities on the interfacial reactions are discussed.This publication has 10 references indexed in Scilit:
- Epitaxial growth of VSi2 on (111) SiJournal of Applied Physics, 1985
- Epitaxial growth of CrSi2 on (111)SiApplied Physics Letters, 1984
- Effects of two-step annealing on the epitaxial growth of CoSi2 on siliconThin Solid Films, 1983
- Ion-beam-induced silicide formation in nickel thin films on siliconThin Solid Films, 1983
- Epitaxial Growth of FeSi2 on (111)SiMRS Proceedings, 1983
- Formation and structure of epitaxial NiSi2 and CoSi2Thin Solid Films, 1982
- Lattice imaging of silicide-silicon interfacesThin Solid Films, 1982
- Solid-state epitaxial growth of deposited Si filmsApplied Physics Letters, 1979
- Iron silicide thin film formation at low temperaturesThin Solid Films, 1975
- Implanted noble gas atoms as diffusion markers in silicide formationThin Solid Films, 1975