Thermal degradation of indium-tin-oxide/p-silicon solar cells
- 1 January 1980
- journal article
- Published by AIP Publishing in Journal of Applied Physics
- Vol. 51 (1) , 527-531
- https://doi.org/10.1063/1.327356
Abstract
Thermal degradation of indium‐tin‐oxide (ITO)/p‐silicon solar cells has been investigated for cells fabricated on both single and polycrystalline silicon. The primary thermal degradation mechanisms was found to be the growth of SiO2 at the ITO/silicon interface resulting from oxygen diffusion through the ITO and not decomposition of the ITO. The degradation rate appears to be limited by surface reaction controlled oxidation since this rate is independent of ITO thickness. The polycrystalline cells were observed to degrade somewhat faster than the single‐crystalline cells. The projected cell life at 50 °C due to thermal failure mechanisms exceeds 105 years for both single‐crystal and polycrystalline cells.This publication has 9 references indexed in Scilit:
- The operation of the semiconductor-insulator-semiconductor solar cell: ExperimentJournal of Applied Physics, 1979
- Auger analysis of ultrathin SiO2 layers on siliconJournal of Applied Physics, 1979
- Fabrication and characterization of indium tin oxide (ITO)/polycrystalline silicon solar cellsApplied Physics Letters, 1978
- SnO2/Si solar cells—heterostructure or Schottky-barrier or MIS-type deviceJournal of Applied Physics, 1978
- The operation of the semiconductor-insulator-semiconductor (SIS) solar cell: TheoryJournal of Applied Physics, 1978
- Effects of heat treatment on the optical and electrical properties of indium–tin oxide filmsJournal of Applied Physics, 1978
- Accelerated life tests of SnO2—Si heterojunction solar cellsIEEE Transactions on Electron Devices, 1977
- Efficient photovoltaic heterojunctions of indium tin oxides on siliconApplied Physics Letters, 1976
- Thermally accelerated aging of semiconductor componentsProceedings of the IEEE, 1974