Preparation of PbTiO3 Thin Films Using a Coating Photolysis Process with ArF Excimer Laser

Publisher Website
Google Scholar
Abstract
TiO2, PbO and PbTiO3 thin films were prepared using the Titanium-2-ethylhexanolate and lead-2-ethylhexanoate coating photolysis process with ArF excimer laser irradiation. The photolysis of Ti-2-ethylhexanolate, Pb-2-ethylhexanoate and mixed Ti-2-ethylhexanolate and Pb-2-ethylhexanoate was investigated by Fourier transform infrared (FT-IR) absorption spectroscopy and X-ray diffraction (XRD). In the case of the one-step ArF irradiation method at 50 mJ/cm2 with a repetition rate of 10 Hz for 5 min, rutile TiO2 and PbTiO3 perovskite phase along with a pyrochlore phase were obtained, while PbO was not obtained. On the other hand, in the case of the two-step ArF irradiation method consisting of preliminary weak irradiation at 10 mJ/cm2 with a repetition rate of 50 Hz for 0.5 min and a stronger irradiation at 50 mJ/cm2 with a repetition rate of 10 Hz for 5 min, anatase TiO2, β-PbO and a single phase of perovskite PbTiO3 were successfully obtained. The crystallization mechanism of PbTiO3 films from the metallorganic precursor is also discussed.