Severe loss of dopant activity due to CHF3+CO2 reactive ion etch damage
- 14 July 1986
- journal article
- research article
- Published by AIP Publishing in Applied Physics Letters
- Vol. 49 (2) , 103-105
- https://doi.org/10.1063/1.97399
Abstract
We report direct evidence from spreading resistance carrier profiling that an effective reduction of up to 5×1019 carriers cm−3 is caused by etching 10–150 nm of doped silicon with a CHF3+CO2 plasma in a commercial hexode reactor. During an 80‐nm etch of bulk p+‐ and n+‐Si, over 99 and 90% respectively of the carriers are trapped or complexed to a depth extending 200 nm from the etched surface. Thermal annealing at 450 °C restores all of the electrical activity, a behavior which is similar to the recovery of phydrogen‐passivated acceptor impurities. More complicated behavior was observed for carrier deactivation of both p+ and n+ implanted junctions, where only partial recovery occurs after a 450 °C anneal. Further annealing at 850 °C does not reactivate any further p‐type dopant, but a 950 °C anneal does increase the n‐type dopant activity.Keywords
This publication has 5 references indexed in Scilit:
- Ar ion beam and CCl4 reactive ion etching: A comparison of etching damage and of damage passivation by hydrogenJournal of Applied Physics, 1985
- Near‐Surface Damage and Contamination after CF 4 / H 2 Reactive Ion Etching of SiJournal of the Electrochemical Society, 1985
- Atomic deuterium passivation of boron acceptor levels in silicon crystalsApplied Physics Letters, 1985
- Reduction of apparent dopant concentration in the surface space charge layer of oxidized silicon by ionizing radiationApplied Physics Letters, 1984
- Plasma-Assisted Etching in MicrofabricationAnnual Review of Materials Science, 1983