Tribological Properties of Hard Carbon Films on Zirconia Ceramics

Open Access
Publisher Website
Google Scholar
Abstract
In this study, the authors investigated the tribological properties of hard diamondlike carbon (DLC) films on magnesia-partially stabilized zirconia (MgO-PSZ) substrates over a wide range of bads, speeds, temperatures, and counterface materials. The films were 2 μm thick and produced by ion-beam deposition at room temperature. Tribological tests were conducted on a ball-on-disk machine with MgO-PSZ balls, in open air of 30 to 50% relative humidity under contact loads of 1 to 50 N, at sliding velocities of 0.1 to 6 m/s, and at temperatures of 400°C. Al2O3 and Si3N4 balls were also rubbed against the DLC-coaled MgO-PSZ disks, primarily to assess their friction and wear performance and to compare it with that of MgO-PSZ balls. A series of long-duration lifetime tests was run at speeds of 1, 2, and 6 m/s under a 5 N load to assess the durability of these DLC films. Results showed that the friction coefficients of MgO-PSZ balls sliding against MgO-PSZ disks were 0.5-0.8, and the average specific wear rates of MgO-PSZ balls ranged from 1 × 10−5 to 5 × 10−4 mm3/N·m, depending on sliding velocity, contact load, and ambient temperature. The friction coefficients of MgO-PSZ balls sliding against the DLC-coaled MgO-PSZ disks ranged from 0.03 to 0.1. The average specific wear rates of MgO-PSZ, balls were reduced by three to four orders of magnitude when rubbed against the DLC-coaled disks. These DLC films could last 1.5 to 4 million cycles, depending on sliding velocity. Scanning electron microscopy and micro-laser Raman spectroscopy were used to elucidate the microstructural and chemical nature of the DLC films and worn surfaces.